Pitting corrosion of the aluminium cladding of spent nuclear fuels stored in light water pools has been observed. To prevent this, coating of the Al cladding with hydrotalcite (HTC) was proposed. This paper presents the effect of chemical bath and processing parameters on microstructure and corrosion behavior of HTC coatings on alloy AA 6061 specimens. The HTC coating from the high temperature nitrate bath was homogeneous, thicker and consisted of well-defined intersecting platelets than that formed from the room temperature carbonate bath. Electrochemical polarization tests carried out with HTC coated AA 6061 specimens in 0.01 M NaCl revealed that specimens coated with HTC from the nitrate bath and further treated in a cerium salt solution were the most resistant to corrosion. Field tests in which un-coated and coated AA 6061 alloy coupons as well as full-size plates were exposed to the IEA-R1 reactor's spent fuel basin for duration of up to 14 months further corroborated the high corrosion resistance imparted by the high temperature HTC + Ce coating. The mechanism by which the HTC coating and cerium protect the Al alloy is discussed.

The high temperature oxidation and erosion-oxidation (E-O) behavior of steels AISI 1020, 304, 310, and 410 were determined. These steels were selected to evaluate the effect of chromium content on its E-O resistance. The oxidation behavior was determined in a thermogravimetric analyzer. A test rig in which a specimen assembly was rotated through a fluidized bed of erodent particles was used to determine the E-O behavior. Alumina powder (200 µm) was used as the erodent. The E-O tests were carried out in the temperature range 25-600 °C, with average particle impact velocities of 3.5 and 15 ms-1 and impact angle of 90°. The oxidation resistance of the steels increased with chromium content. The E-O behavior of the steels was determined as wastage. The E-O wastage of the steels exposed to particle impact at low velocity was low but increased with temperature above 300 °C. The E-O wastage of the different steels exposed to particle impact at high velocity was quite similar. The wastage increased with increase in temperature above 500 °C. The increases in E-O wastage of the steels observed at temperatures above 300, 400 or 500 °C, depending on the steel, were due mainly to a transition in the dominant wastage process, from 'erosion' to 'erosion-oxidation'.

Rare earths (RE) have been used to increase high temperature oxidation resistance of chromium dioxide and alumina forming alloys. The RE can be added as elements (or oxides) to the alloys or applied as an oxide coating to the alloy surface. RE oxide gels, obtained by the sol-gel technique, were used to coat Fe-20Cr specimens prior to cyclic oxidation tests in the temperature range RT-900 °C. The cyclic oxidation resistance of the alloy increased with time required to reach a specific chromium dioxide layer thickness, and this was influenced by RE ion radius, the coating morphology and coverage. Extended cyclic oxidation tests from peak temperatures of 900, 1000 and 1100 °C at cooling rates of 330 and 1000 °C/s revealed the marked influence of La2O3 coatings. The role of RE in increasing overall oxidation resistance of chromium dioxide forming alloys is discussed.

The addition of small quantities of reactive elements such as rare earths (RE) to chromia or alumina forming alloys improves the high temperature oxidation resistance. Traditionally, these elements are alloying additions or are added as oxides to form a dispersion. The alloys can also be coated with RE oxides. Several methods can be used to coat alloy substrates with RE oxides and the sol-gel process is considered to be quite efficient, as it generates the very small oxide particles. This paper presents the influence of surface coatings of Ce, La, Pr, and Y oxide gels on the oxidation behavior of an Fe-20Cr alloy at 1000 °C. The morphology of the rare earth (RE) oxide coatings varied with the nature of RE. The oxidation rate of RE oxide coated Fe-20Cr was significantly less than that of the uncoated alloy. The extent of influence the RE oxide coating exercised on the oxidation rate decreased in the following order: La, Ce, Pr, Y. The scale formed in the presence of RE oxide was very thin, fine grained and adherent chromia. A direct correlation between rare earth ion radius and the extent of influence on chromia growth rate at 1000 °C was observed.